Polymer Encapsulants for Photovoltaic Modules: Electrical Insulation Performance and Long-Term Durability under Accelerated UV Exposure
Abstract: Influence on the reliability and service life of PV modules is a major issue, which is influenced by the encapsulant degradation in long-term exposure to the sun's ultraviolet (UV) radiation. A systematic accelerated UV aging study of Ethylene Vinyl Acetate (EVA), Polyolefin Elastomer (POE), and Polyvinyl Butyral (PVB) films under IEC 61215-2:2021 specified test chamber conditions of Q-UV is conducted. The material properties were tested at various exposure intervals including …
Published in Journal of Polymer & Composites · Vol. 14, Issue 3, 2026 · pp. 384–408 Read article
-
Corrosion and Corrosion Protection of Unio in Carbonic Acid Medium
Abstract: Unio is a calciferous animal, and its outer surface is made of calcium carbonate. It usually happens in sources of sweet water. They create carbonic acid by absorbing carbon dioxide. It changes the pH of sweet water sources thus water becomes acidic. It develops corrosive environment for Unio. Carbonic acid interacts with Unio to form corrosion cells on the interface of Unio. This acid oxidizes calcium carbonate into calcium ions …
Published in Journal of Water Pollution & Purification Research · Vol. 12, Issue 1, 2025 · pp. 22–31 Read article
-
Polymeric Coating Applied for Corrosion Protection of Mild Steel in Corrosive Medium
Abstract: Mild steel is coated with a polymer layer of polybutadiene for protection. However, this coating does not effectively safeguard the metal in environments containing moisture, sulphur dioxide, or chloride. These pollutants interact with the polybutadiene-coated surface, creating a highly corrosive atmosphere. Moisture condenses on the coated metal surface and absorbs sulphur dioxide, forming sulphuric acid. This acid initiates both chemical and electrochemical reactions with the polymer-coated metal, accelerating the corrosion …
Published in International Journal of Advance in Molecular Engineering · Vol. 3, Issue 2, 2025 · pp. 49–53 Read article