3 articles for “AA6082”
-
Investigation of Residual Stress, and corrosion behavior of AA6082/Al 2 O 3 /C/ Si 3 N 4 Composite Material
Abstract: The main objective of the current study was to create AA6082/ Al2O3/C/Si3N4 Composite Material by the use of stir casting. The properties of the AA6082/ Al2O3/C/ Si3N4 Composite Material shown a significant improvement, with a micro-hardness rise of 13.5% and a residual stress decrease of 60%. As the testing parameters were increased, the residual stress of the AA6082/ Al2O3/C/ Si3N4 Composite Material rapidly decreased from -65MPa to -15MPa. An electromagnetic …
Published in Journal of Polymer & Composites · Vol. 13, Issue 1, 2025 · pp. 1104–1109 Read article
-
Parametric optimization of COF of fabricated AA6082/Si3N4/C/Al2O3 composite
Abstract: In the present experimental investigation AA6082/Si3N4/C/Al2O3 composite was successfully fabri-cated using stir casting technique combined with electromagnetic stirrer for wear resistance applica-tions. The produced AA6082/Si3N4/C/Al2O3 composite exhibits improved tribological and me-chanical and properties, according to the experimental results. The generated composite has a micro-hardness range of 60 to 110 HV and an average UTS of 150 to 200 MPa. The tribological perfor-mance was evaluated using a pin on disc tribometer. …
Published in Journal of Polymer & Composites · Vol. 12, Issue 2, 2024 · pp. 144–152 Read article
-
Numerical Studies on Deep Drawability of the Aluminium Alloy, AA6082 and Parameters Affecting It
Abstract: Deep drawing is a metal forming operation used for manufacturing sheet-metal components for application in the automobile, aerospace, and packaging industries. The objective of the present work was to study the various parameters influencing the drawability of AA6082. The deep-drawing process was modeled and simulated in Ls-Dyna Pre-Post(R) V4.6.17 software. The tensile test was performed according to the ASTM-E8M standard on AA6082-T6 material and subsequently annealed to attain higher ductility. …
Published in Journal of Polymer & Composites Read article