Catalyst-Driven Degradation and Failure Analysis of Intergranular Cracking in 316H Studded Pipes under Refinery Heat Recovery Conditions
Abstract: A failure analysis investigation was carried out on a high-temperature studded pipe used in a convection module for heat recovery in an oil and gas refinery application after leakage was detected during pre-commissioning hydrotesting. The investigated pipe was manufactured from AISI 316H austenitic stainless steel, and carbon steel studs had been joined to its outer surface by high-frequency resistance welding. Two leaks were reported in the pipe under investigation, and …