An Investigation into the VariablesInfluencing the Densification of Spark Plasma Sintered, 40 Weight Percent Ni-Fe Nano PowderBy Prashant Sharma
Abstract: The mechanical alloying process that included high-energy ball milling resulted in particle sizes of 25 mm and 80 mm on average for the Ni-Fe alloy that included 40 percent Ni. At room temperature, highenergy planetary ball milling was carried out over timespan ranging from 15 hours to 60 hours. All of the samples were sintered at the same conditions, which included a temperature of 650 degrees Celsius and a pressure …